性能项目测试条件测试方法数值/描述单位机械性能拉伸强度(引张强度)

ASTM D638/ISO 527180kg/cm2(MPa)[Lb/in2]断裂伸长率

ASTM D638/ISO 527

%拉伸模量

ASTM D638/ISO 5278600kg/cm2(MPa)[Lb/in2]拉伸屈服伸长率(延伸率)

ASTM D638/ISO 527

%拉伸断裂伸长率(延伸率)

ASTM D638/ISO 527

%弯曲模量(弯曲弹性率)

ASTM D790/ISO 1787600kg·cm/cm(J/M)ft·lb/in弯曲强度

ASTM D790/ISO 178260kg·cm/cm(J/M)ft·lb/in洛氏硬度

ASTM D785

IZOD 缺口冲击强度1/4" 23℃ASTM D256/ISO 179

kg·cm/cm(J/M)ft·lb/in1/4" -30℃ASTM D256/ISO 179

kg·cm/cm(J/M)ft·lb/in1/8" 23℃ASTM D256/ISO 179

kg·cm/cm(J/M)ft·lb/in1/8" -30℃ASTM D256/ISO 179

kg·cm/cm(J/M)ft·lb/inCharpy冲击强度23℃ （缺口）ASTM D256/ISO 179

kg·cm/cm(J/M)ft·lb/in-30℃（缺口）ASTM D256/ISO 179

kg·cm/cm(J/M)ft·lb/in23℃（无缺口）ASTM D256/ISO 179

kg·cm/cm(J/M)ft·lb/in-30℃（无缺口）ASTM D256/ISO 179

kg·cm/cm(J/M)ft·lb/in物性性能比重（密度）

ASTM D792/ISO

成型收缩率

ASTM D955/0.55%熔融指数（流动系数）200℃/5kgASTM D1238/ISO 1133

g/10min220℃/10kgASTM D1238/ISO 1133

g/10min吸水率 23℃/24H

ASTM D570/ISO 62

%热性能热变形温度退火ASTM D648/ISO 75250℃（℉）未退火ASTM D648/ISO 75250℃（℉）维卡软化点

ASTM D1525/ISO R306

℃（℉）熔点

-260℃（℉）燃烧性（率）

UL94

线性膨胀系数

ASTM D696/ISO 11359

mm/mm.℃电气性能介电常数100HZASTM D150/IEC 60250

1MHZASTM D150/IEC 60250

体积电阻率

ASTM D257/IEC 600931E 13Ω.cm表面电阻率

ASTM D257/IEC 60093

Ω耐电弧性

ASTM D495/IEC 60112

加工条件干燥条件

80℃加工温度射嘴

℃料筒前段

℃料筒中段

℃料筒后段

℃熔体温度

280~305℃模具温度

80~90℃压力注塑压力

Mpa保压压力

Mpa背压

Mpa螺杆转速

rpm其他备注高机械强度、刚度和热稳定性，低温抗冲击性、滑动摩擦性颜色

特性多种工程部件和机械零件（如优质电绝缘材料）及多种特殊应用